Özgün Başlık Low Temperature Oxidation of Turkish Aşkale Lignite : Effects of Particle Size and Temperature Yazarlar Aysel Küçük, Yücel Kadıoğlu Dergi Adı Sakarya Üniversitesi Fen Edebiyat Dergisi Cilt 2008, Cilt 10, Sayı 2, ss. 43-64 Anahtar Kelimeler Oxygen-containing functional groups ; FT-IR Spectroscopy ; Wet chemical analysis Özet The chemical changes occurring during the low-temperature oxidation of Aşkale lignite (Turkey) in air has been investigated with both wet chemical analysis and FT-IR spectroscopy. The oxidation tests were carried out at elevated temperatures, 40, 70, 120, 170, 200, 250 and 300 °C for the samples with three different particle sizes, which were-125, 125-250 and 250-710 µm size fractions. There were changes in the hydroxyl and the carboxyl contents, depending on the temperature of oxidation. Başlık (Yabancı Dil) Türk Aşkale Linyitinin Düşük Sıcaklık Oksidasyonu : Partikül Boyutu ve Sıcaklığın Etkisi Anahtar Kelimeler (Yabancı Dil) Oksijen İçeren Fonksiyonel Gruplar ; FT-IR Spektroskopisi ; Islak Kimyasal Analizler Özet (Yabancı Dil) Aşkale Linyitinin (Türkiye) düşük sıcaklık oksitlenmesi sırasında meydana gelen kimyasal değişiklikler, hem ıslak kimyasal analizler hem de FT-IR spektroskopisi ile incelenmiştir. Oksidasyon testleri, -125, 125 - 250 ve 250 - 710 µm partikül boyutuna sahip, üç farklı partikül boyutlu numuneler için 40, 70, 120, 170, 200, 250 ve 300 °C'lerde yükseltilmiş sıcaklıklarda yürütülmüştür. Oksidasyon sıcaklığına bağlı olarak, hidroksil ve karboksil muhtevalarında değişiklikler olmuştur |